Product Details:
Payment & Shipping Terms:
|
Shape: | Round, Square Or Customized | Color: | Black, White, Brown, Green Or Others |
---|---|---|---|
Feature: | High Temperature And Ozone Resistance | Hardness: | 60-90 Shore A |
Processing Method: | Molding Or Extrusion | Material: | Fluoroelastomer Viton A, Viton B |
Size: | 1mm To 35mm | Packing: | PE Film + Carton |
High Light: | 1mm solid round rubber cord,90 Shore A Extruded Rubber Cord,35mm Extruded Rubber Cord |
High Temperature Ozone Sealing Hose Rubber Round And Square Cord
Description:
Ozone resistance rubber is a collective name which no crack when rubber exposed to ozone. Ozonation is
the main reason that make rubber be cracked.
Ozone resistance rubber: EPDM, Chlorosulfonated polyethylene, Polyurethane, Silicone and Fluoroelastomer FKM.
Ozone resistance rubber products: Hose, O ring, Sealing strip, Cuff, Cord,
Fluoroelastomer ozone property: FKM have excellent weather resistance and ozone resistance. Dupon
Viton A grade rubber sealing part have good performance after 10 years based on natual environment, and
in 0.01% air it also not visible crake after 45 days.
FKM also have very good high temperature resistance, so FKM is a very good choice for heat + ozone sealings.
Material Type: Viton A Viton B grade. BPAF cured copolymer and terpolymer.
Temperature range: -20 to 250 degree in long time
Sealing shapes: Round and square or other customized
Size: 1mm to 40mm
Appearance: solid rubber cord
Packing: Based on size and should be easy packing.
Application: Any ozone and high temperature environment
Typical property | |||||
Test item | Result | Test standard | |||
Hardness, Shore A | 60-90 Shore A | GB/T 531.1-2008 | |||
Tensile strength,Mpa | 8-15 | GB/T 528-2009 | |||
Elongation at break, % | 150-300 |