60 Shore A Acid Resistance FKM Rubber Material

China Chengdu Eson New Material Co., Ltd. certification
China Chengdu Eson New Material Co., Ltd. certification
I'm Online Chat Now

60 Shore A Acid Resistance FKM Rubber Material

60 Shore A Acid Resistance FKM Rubber Material
60 Shore A Acid Resistance FKM Rubber Material 60 Shore A Acid Resistance FKM Rubber Material

Large Image :  60 Shore A Acid Resistance FKM Rubber Material

Product Details:
Place of Origin: CHINA
Brand Name: ESON
Certification: ISO9001
Model Number: AF70
Payment & Shipping Terms:
Minimum Order Quantity: 25KG
Price: Negotiable
Packaging Details: 25kg per carton
Delivery Time: 3-9 working days
Payment Terms: T/T, Ali
Supply Ability: 20T per month
Detailed Product Description
Material: FEPM Aflas Compound Hardness: 60-90 Shore A
Color: Black, Brown, Red Or Any Application: Mechinary, Military, Auto And Others
End Product: O Ring, Gasket, Valve, Oil Seal, Cable Feature: Hot Water Resistance, Steam Resistance, Sodium Hydroxide Resistance,ammonium Hudroxide Resistance
Name: Acid PEFM Material MOQ: 25kg
High Light:

PEFM FKM Precompound And Compound

,

Aflas FKM Precompound And Compound

,

17.9Mpa FEPM Aflas compound

FEPM High Temperature Resistance Steam Resistance Aflas O Ring Rubber Material Compound

 

Material type: Tetrafluoroethylene - propylene copolymer TFE/P commonly known as tetrafluororubber. It is an alternate copolymer of tetrafluoroethylene and propyleneAdvantages: Good stability, chemical resistance, especially high concentration acid, alkali, strong oxidant performance, high pressure steam resistance, water resistance and electrical insulation performance, low air permeability, service temperature -400~200 ℃

 

Products: sheet, gasket, rubber hose, roller, O-ring, diaphragm, valve sheet, wire, bottle stopper and other products, widely used in automotive, petroleum, textile, chemical and food industry

 

Description:Compared with type 26 fluororubber, tetrafluororubber has better acid and alkaline resistance. After soaking in 70℃ nitric acid (mass fraction 0.6) for 3 days, the appearance of the sample was unchanged, while the type 26 fluororubber was damaged. After soaking in the acid base (100℃×72 h), the volume change rates of tetrafluoro-rubber were 4.2%(sulfuric acid with mass fraction 0.96), 2L %(nitric acid with mass fraction 0.6) and 0.1%(sodium hydroxide solution with mass fraction o.5), respectively. The acid and alkaline resistance of tetrafluororubber is superior to that of type 23 fluororubber, which has the best acid and alkaline resistance. After soaking in nitric acid (mass fraction 0.98) at room temperature, the mass change rate of fluororubber is as follows. Domestic 2311 fluorinated rubber 9.7%(soaked for 24 h) and 25.3%(soaked for 144 h), American KEL-F5500 fluorinated rubber 10.7%(soaked for 24 h), domestic tetrafluoro-fluorinated rubber SinoflastP-2 0.6%(soaked for 168 h). After being immersed in sodium hydroxide solution (mass fraction is 0.5) for 168h at room temperature, the volume change rate of tetrafluor is as follows: SinoflastP-2 0.03%, JSRAflasl50 1.2%. In addition, the processability of 23 type fluorine rubber is poorer, difficult to extrusion, extrusion semi-finished product surface quality is poor, and four fluorine rubber extrusion speed is 23 c type 5 times of fluorine rubber, extrusion semi-finished good appearance, four fluorine rubber relative density is 1.55 c, below 23 type fluorine rubber (relative density is 1.85), so consider technology, performance and cost, 23 type fluorine rubber may be four fluorine rubber instead of c. Unique compression resistance to permanent deformation performance. Tetrafluororubber not only has excellent compressive permanent deformation performance at high temperature, but also does not decrease its deformation recovery performance even if compressed for a long time at high temperature, while other fluororubbers increase the compression permanent deformation with the extension of time. Tetrafluororubber unique compression resistance permanent deformation performance for its use in seals is very advantageous

 

Data sheet:

Aflas raw gum chemical resistance data
Hot water 180℃ 168h Tensile strength ratention rate, % 88
Elongation retention rate,% 104
Hardness change, Shore A -4
Volume change, % 14
720h Tensile strength ratention rate, % 85
Elongation retention rate,% 100
Hardness change, Shore A -5
Volume change, % 16
Steam 180℃ 168h Tensile strength ratention rate, % 90
Elongation retention rate,% 107
Hardness change, Shore A -3
Volume change, % 8
720h Tensile strength ratention rate, % 92
Elongation retention rate,% 88
Hardness change, Shore A -3
Volume change, % 10
50% Sodium Hydroxide 168h Tensile strength ratention rate, % 102
Elongation retention rate,% 100
Hardness change, Shore A +1
Volume change, % 0
720h Tensile strength ratention rate, % 100
Elongation retention rate,% 100
Hardness change, Shore A 0
Volume change, % -1
28% ammonium hudroxide 70℃ 168h Tensile strength ratention rate, % 96
Elongation retention rate,% 98
Hardness change, Shore A -1
Volume change, % 1
720h Tensile strength ratention rate, % 99
Elongation retention rate,% 94
Hardness change, Shore A -1
Volume change, % 1
Aflas compound QF-AF70
Press cure: sheet 170℃ @ 10 min. Post cure: 200℃@4h
Typical property Unit Test method Test result
Hardness Shore A D2240 74
Tensile strength Mpa D412 17.9
Elongation at break % D412 283
Tear strength kg/cm D612 34
Modulus 100% Mpa D412 5.5
Specific gravity g/cm3 / 1.542
Heat resistance 250℃@70h
Hardness change Shore A D573 +2
Tensile strength change % D573 -18
Elongation change % D573 +15
Volume change % D573 -7.5
Heat resistance 275℃@70h
Hardness change Shore A D573 +1
Tensile strength change % D573 -50
Elongation change % D573 +17
Volume change % D573 -11.3
Liquid 101# 200℃@70h
Hardness change Shore A D471 -17
Tensile strength change % D471 -25
Elongation change % D471 -7
Volume change % D471 +29.6
Heat resistance 275℃@70h
Hardness change Shore A D471 -32
Tensile strength change % D471 -63
Elongation change % D471 -51
Volume change % D471 -81.3

 

Picture show:

60 Shore A Acid Resistance FKM Rubber Material 0

60 Shore A Acid Resistance FKM Rubber Material 1

 

Contact Details
Chengdu Eson New Material Co., Ltd.

Contact Person: Lily Luo

Tel: 86-15680650120

Send your inquiry directly to us (0 / 3000)