Home ProductsFKM Rubber Material

Liquid Coating FKM Rubber Material Black Used In Metal

China Chengdu Eson New Material Co., Ltd. certification
China Chengdu Eson New Material Co., Ltd. certification
I'm Online Chat Now

Liquid Coating FKM Rubber Material Black Used In Metal

Liquid Coating FKM Rubber Material Black Used In Metal
Liquid Coating FKM Rubber Material Black Used In Metal Liquid Coating FKM Rubber Material Black Used In Metal

Large Image :  Liquid Coating FKM Rubber Material Black Used In Metal

Product Details:
Place of Origin: Sichuan, China
Brand Name: Eson
Certification: ISO9001
Model Number: ES3035
Payment & Shipping Terms:
Minimum Order Quantity: 25kg
Price: Negotiable
Packaging Details: Carton+ Pallet
Delivery Time: 7-15 Days
Payment Terms: T/T,Ali Trade Insurance
Supply Ability: 20 Ton/Tons per Month
Detailed Product Description
Name: FKM Liquid Coating Material Size: Accept Customize
Temperature Range: -40℃-280℃ Color: Black,any Other
Coating Method: Brush Coating, Roller Coating, Silk-screen Coating,etc Length: Accept Customize
Feature: High Stability, Oil Resistance, Solvent Resistance,etc Material: Fluoroelastomer Rubber
High Light:

15Mpa FKM rubber compounds

,

Black FKM Precompound And Compound

,

15Mpa FKM Precompound And Compound

Coated On Metal Fluoroelastomer Rubber FKM Liquid Coating Material

 

AT & BT series are monocomponent high-temperature baked F-rubber (rubber cement) coating composition.

 

Product features:

  • Adhesive force reaches class I (crossing method)
  • High stability, without gel in 3 months generally
  • Be able to compound with other materials, forming composite material.
  • Excellent performances of oil resistance, solvent resistance, acid & alkali resistant and other special mediums
  • Can be used under the temperature of -40℃-280℃

Typical Property( tested after 100% cured)

  SFAT-H SFAT-X SFBT-H SFBT-X
Apperance Black Colorful Black Colorful
Density,g/cm3 1.9 2.09 1.96 2.15
Hardness, Shore A 50-90 50-90 50-90 50-90
Tear strength, Mpa 6-15 6-14 6.5-16.5 6-16
Elongation at break, % 165-450 160-240 170-450 165-450
Compression set, 200℃*70h, %  15-25 15-24 23-28 23-28
Volume change, Methanlo resistance,% --- --- --- ---
Volume change, 3# oil resistance,% ≤6 ≤6 ≤4 ≤4
Low temperature brittleness, ℃ -23 -23 -20 -20

 

Method of application:

Stir evenly before applying, use screen cloth with mesh of 200,

use butyl ester or isophorone for dilution if with high viscosity,

isophorone is recommended to use for silk screen coating or high-temperature weather.

The coating surface shall be treated with chemical or physical method,

metal surface shall be derusted and degreased,

plastic surface shall be degreased and polished first and then greased again.

Acetone is recommended for greasing, solvents are different for

different plastics, glass fiber, polyester, Kevlar with large density shall be greased,

cotton cloth and nylon can be coated directly.

Coating method: brush coating, roller coating, silk-screen coating, dip-coating etc.

Dip-coating or roller coating is recommended for fiber cloth.

Solidification: air-drying and stoving within 80℃, drying rate should not be too fast, otherwise,

surface blisters shall easily form especially for thick coating.

5~10 minutes of solidification within temperature range of 165~200℃for thin coating.

Solidification within temperature range of 165~200℃ and pressure above 3kgs

for coating with more than 0.3mm thickness and fiber cloth coating.

For better performance, all products should be solidified again in 4~20 hours within temperature range of 200~250℃.


Pictures show:

 

 

Liquid Coating FKM Rubber Material Black Used In Metal 0Liquid Coating FKM Rubber Material Black Used In Metal 1